Cellulose derivative, thermo-molding material, molded body and method for preparation thereof, and case for electric and electronic devices

ABSTRACT

A thermo-molding material contains a water-insoluble cellulose derivative, wherein the water-insoluble cellulose derivative comprises: A) a hydrocarbon group; B) a group containing an acyl group: —CO—R B1  and an alkyleneoxy group: —R B2 —O— (R B1  represents a hydrocarbon group, and R B2  represents an alkylene group having 3 carbon atoms); and C) an acyl group: —CO—R C  (R C  represents a hydrocarbon group).

TECHNICAL FIELD

The present invention relates to a cellulose derivative, a thermo-molding material, a molded body and a method for preparation thereof, and a case for electric and electronic devices.

BACKGROUND ART

In members constituting electric and electronic devices such as a copy machine and a printer, various materials are used in consideration of characteristics and functions required for the members. For example, for a member (case) that plays a role of receiving a driving apparatus of an electric and electronic device or the like, and protecting the driving apparatus, a large amount of PC (polycarbonate), an ABS (acrylonitrile-butadiene-styrene) resin, PC/ABS or the like are generally used (Patent Document 1). These resins are prepared by reacting compounds obtained by using petroleum as a raw material.

By the way, fossil resources, such as petroleum, coal and natural gas, include carbon fixed under the earth over a long period of time as a main component. In the case where carbon dioxide is discharged into the atmosphere by combusting such fossil resources or products using the fossil resources as a raw material, carbon that does not exist in the atmosphere but is fixed deeply under the earth, is rapidly discharged as carbon dioxide, and thus, carbon dioxide in the atmosphere is largely increased, thereby causing a global warming. Accordingly, a polymer such as ABS and PC having petroleum, which is a fossil resource, as a raw material has excellent properties as a material of the member for electric and electronic devices, but since petroleum, which is a fossil resource, is used as the raw material, it is preferable that the amount used is decreased from the standpoint of preventing the global warming.

Meanwhile, a plant-derived resin is basically generated by a photosynthesis reaction using water and carbon dioxide in the atmosphere as raw materials by plants. Therefore, there is an opinion that, although carbon dioxide is generated by combusting a plant-derived resin, the carbon dioxide corresponds to carbon dioxide previously existing in the atmosphere, and thus, the balance of carbon dioxide in the atmosphere becomes zero-sum, such that the total amount of CO₂ in the atmosphere is not increased. Based on this opinion, the plant-derived resin is called a “carbon neutral” material. The use of the carbon neutral material instead of the petroleum-derived resin has gained importance in preventing the current global warming.

Therefore, in the PC polymer, there is proposed a method for decreasing petroleum-derived resources by using plant-derived resources such as starch as a portion of the petroleum-derived raw materials (Patent Document 2).

However, there is a need for further improvement from the standpoint of targeting a more perfect carbon neutral material.

As a known cellulose derivative, hydroxypropylmethylacetyl cellulose is described in Patent Documents 3 and 4. Patent Documents 3 and 4 describe that the hydroxypropylmethylacetyl cellulose is useful as an additive for reducing the vapor pressure of organic solvents which are easily volatilized. Further, for the degree of substitution of each substituent in the hydroxypropylmethylacetyl cellulose described in Patent Documents 3 and 4, for example, it is described that a molar degree of substitution (MS) of a hydroxypropyl group is in a range of about 2 to about 8, a degree of substitution of a methyl group is in a range of about 0.1 to about 1, and a degree of substitution of an acetyl group is in a range of about 0.8 to about 2.5.

Moreover, as a use of coating of medicaments, hydroxypropylmethylpropyl cellulose, hydroxypropylmethylbutyl cellulose, and the like (Patent Document 5), and hydroxypropyl methylcellulose phthalate, and the like, (Patent Document 6) are disclosed.

RELATED ART Patent Document

Patent Document 1: Japanese Patent Application Laid-Open No. Sho 56-55425

Patent Document 2: Japanese Patent Application Laid-Open No. 2008-24919

Patent Document 3: U.S. Pat. No. 3,979,179

Patent Document 4: U.S. Pat. No. 3,940,384

Patent Document 5: International Publication No. WO 09/010,837

Patent Document 6: Japanese Patent No. 3017412

DISCLOSURE OF INVENTION Problems to be Solved by the Invention

The present inventors paid an attention on using cellulose as a carbon neutral resin. However, cellulose, generally having no thermoplasticity, is not appropriate for molding processing due to difficulty in molding by heating and the like. In addition, even if thermoplasticity could be imparted to cellulose, there still is the problem that strength such as impact resistance is largely deteriorated. Furthermore, there is also room for improvement on heat resistance. For example, the cellulose derivatives described in Patent Documents 3, 4 and 6 are water-soluble or swellable, and thus, are not preferable as a molding material. Further, although the cellulose derivative described in Patent Document 5 is described as water-soluble, there is only a description in the text, and there are no specific disclosures on a synthesis method, a use form thereof, and the like, in the form of Example, and the like.

An object of the present invention is to provide a cellulose derivative and a thermo-molding material that have good thermoplasticity, strength and heat resistance, and are suitable for molding processing.

Means for Solving the Problems

The present inventors found out, in consideration of a molecular structure of cellulose, that good thermoplasticity, impact resistance and heat resistance are exhibited when using a cellulose derivative having a specific structure as the cellulose, thereby accomplishing the present invention.

That is, the above object may be accomplished by the following means.

-   [1] A thermo-molding material comprising a water-insoluble cellulose     derivative, wherein the water-insoluble cellulose derivative     comprises:

A) a hydrocarbon group;

B) a group containing an acyl group: —CO—R_(B1) and an alkyleneoxy group: —R_(B2)—O— (R_(B1) represents a hydrocarbon group, and R_(B2) represents an alkylene group having 3 carbon atoms); and

C) an acyl group: —CO—R_(C) (R_(C) represents a hydrocarbon group).

-   [2] The thermo-molding material of [1] above, wherein A) the     hydrocarbon group is an alkyl group having 1 to 4 carbon atoms. -   [3] The thermo-molding material of [1] above, wherein A) the     hydrocarbon group is a methyl group or an ethyl group. -   [4] The thermo-molding material of any one of [1] to [3] above,     wherein each of R_(B1) and R_(C) independently represents an alkyl     group or an aryl group. -   [5] The thermo-molding material of any one of [1] to [4] above,     wherein each of R_(B1) and R_(C) independently represents a methyl     group, an ethyl group, or a propyl group. -   [6] The thermo-molding material of any one of [1] to [5] above,     wherein the alkyleneoxy group is a group represented by the     following formula (1) or formula (2).

-   [7] The thermo-molding material of any one of [1] to [6] above,     wherein B) the group containing an acyl group: —CO—R_(B1) and an     alkyleneoxy group: —R_(B2)—O— is a group containing a structure     represented by the following Formula (3):

(wherein, R_(B) represents a hydrocarbon group, and R_(B2) represents an alkylene group having 3 carbon atoms.)

-   [8] The thermo-molding material of any one of [1] to [7] above,     wherein the cellulose derivative has substantially no carboxyl     group. -   [9] A water-insoluble cellulose derivative, comprising

a1) an ethyl group;

b1) a group containing an acyl group: —CO—Rb1 and an alkyleneoxy group: —Rb2-O— (Rb1 represents a hydrocarbon group, and Rb2 represents an alkylene group having 3 carbon atoms); and

c1) an acyl group: —CO—Rc (Rc represents a hydrocarbon group).

-   [10] A water-insoluble cellulose derivative, comprising

a2) a methyl group;

b2) a group containing an acyl group: —CO—Rb1 and an alkyleneoxy group: —Rb2-O— (Rb1 represents a hydrocarbon group, and Rb2 represents an alkylene group having 3 carbon atoms); and

c2) an acyl group: —CO—Rc (Rc represents a hydrocarbon group),

wherein a degree of substitution of a2) the methyl group is 1.1 or more and a molar degree of substitution (MS) of the alkyleneoxy group is 1.5 or less.

-   [11] The cellulose derivative of [9] or [10] above, wherein each of     Rb1 and Rc independently represents a methyl group, an ethyl group,     or a propyl group. -   [12] The cellulose derivative according of any one of [9] to [11]     above, wherein the cellulose derivative has substantially no     carboxyl group. -   [13] A case for electric and electronic devices, composed of a     molding body obtained by molding the thermo-molding material of any     one of [1] to [8] above or the cellulose derivative of any one of     [9] to [12] above. -   [14] A method for manufacturing a molded body, comprising:

a step of heating and molding the thermo-molding material of any one of [1] to [8] above or the cellulose derivative of any one of [9] to [12] above.

Effects of the Invention

The cellulose derivative or thermo-molding material of the present invention has excellent thermoplasticity, and thus, may be manufactured into a molded body. Further, a molded body formed by the cellulose derivative or thermo-molding material of the present invention has good impact resistance, heat resistance, and the like, and thus, may be used appropriately as component parts such as automobiles, home electric appliances, electric and electronic devices, mechanical parts, materials for housing and construction, and the like. In addition, the cellulose derivative or thermo-molding material of the present invention is a plant-derived resin and is a material which may contribute to the prevention of global warming, and thus, the cellulose derivative or thermo-molding material of the present invention may replace petroleum-derived resins of the related art. Furthermore, the cellulose derivative and thermo-molding material of the present invention exhibit biodegradability, and thus, are expected to be used as a material with less environmental load.

EMBODIMENTS FOR CARRYING OUT THE INVENTION

A thermo-molding material of the present invention contains a water-insoluble cellulose derivative containing A) a hydrocarbon group, B) a group containing an acyl group: —CO—R_(B1) and an alkyleneoxy group: —R_(B2) —O— (R_(B1) represents a hydrocarbon group and R_(B2) represents an alkylene group having 3 carbon atoms), and C) an acyl group: —CO—R_(C) (R_(C) represents a hydrocarbon group).

Hereinafter, the present invention will be described in detail.

1. Cellulose Derivative

A cellulose derivative contained in the thermo-molding material of the present invention has:

A) a hydrocarbon group,

B) a group containing an acyl group: —CO—R_(B1) and an alkyleneoxy group: —R_(B2)—O—(R_(B1) represents a hydrocarbon group and R_(B2) represents an alkylene group having 3 carbon atoms), and

C) an acyl group: —CO—R_(c) (R_(c) represents a hydrocarbon group).

That is, the cellulose derivative in the present invention is obtained by substituting at least a portion of hydrogen atoms of a hydroxyl group contained in the cellulose {(C₆H₁₀ O₅)_(n)} with A) a hydrocarbon group, B) a group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—), and C) an acyl group (—CO—R_(c)).

More specifically, the cellulose derivative in the present invention has a repeating unit represented by the following Formula (A).

In the formula, each of R², R³ and R⁶ independently represents a hydrogen atom, A) a hydrocarbon group, B) a group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—), or C) an acyl group (—CO—R_(C)). Each of R_(B1) and R_(C) independently represents a hydrocarbon group. R_(B2) represents an alkylene group having 3 carbon atoms. However, at least a portion of R², R³ and R⁶ represents a hydrocarbon group and at least a portion of R², R³ and R⁶ represents a group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—), and at least a portion of R², R³ and R⁶ represents an acyl group (—CO—R_(C)).

As described above, the cellulose derivative of the present invention may exhibit thermoplasticity because at least a portion of the hydroxyl groups of the β-glucose ring is etherified and esterified by A) the hydrocarbon group, B) the group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—), and C) the acyl group (—CO—R_(C)), thereby being appropriate for molding processing.

Further, the cellulose derivative is water-insoluble and may also exhibit excellent strength and heat resistance as a molded body. Furthermore, since cellulose is a completely plant-derived component, cellulose is carbon neutral, and may greatly reduce the environmental load.

As used herein, “water-insoluble” means that the solubility thereof in 100 parts by mass of water (pH 3 to 11) at 25° C. is 5 parts by mass or less.

As used herein, “cellulose” means a polymer compound in which a plurality of glucoses are linked by β-1,4-glycoside bonds with the hydroxyl groups bonded to the carbon atoms at the 2-, 3- and 6-position of each glucose ring of the cellulose being unsubstituted. Further, “hydroxyl groups contained in cellulose” represents hydroxyl groups which are bonded to the carbon atoms at the 2-, 3- and 6-position of each glucose ring of the cellulose.

The cellulose derivative in the present invention contains:

at least one group in which a hydrogen atom of a hydroxyl group contained in the cellulose is substituted by A) a hydrocarbon group,

at least one group in which a hydrogen atom of a hydroxyl group contained in the cellulose is substituted by B) a group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—), and

at least one group in which a hydrogen atom of a hydroxyl group contained in the cellulose is substituted by C) an acyl group (—CO—R_(C)).

The cellulose derivative of the present invention may have two or more different kinds of groups as the A) to C).

The cellulose derivative may contain A) the hydrocarbon group, B) the group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—), and C) the acyl group (—CO—R_(C)) at any one part of the whole thereof, and may be composed of the same repeating units and of plural kinds of repeating units. In addition, it is not necessary for the cellulose derivative to contain all the substituents of the A) to C) in a single repeating unit.

As more specific aspects, there may be the following aspects.

(1) A cellulose derivative composed of a repeating unit in which a portion of R², R³ and R⁶ is substituted with A) a hydrocarbon group, a repeating unit in which a portion of R², R³ and R⁶ is substituted with B) a group containing an acyl group (—CO—R_(B1)) and an alkylene group (—R_(B2)—O—), and a repeating unit in which a portion of R², R³ and R⁶ is substituted with C) an acyl group (—CO—R_(C)).

(2) A cellulose derivative composed of the same repeating units in which any one of R², R³ and R⁶ in one repeating unit is substituted with A) a hydrocarbon group, B) a group containing an acyl group (—CO—R_(B1)) and an ethyleneoxy group (—R_(B2)—O—), and C) an acyl group (—CO—R_(C)) (that is, having all the substituents of the A) to C) in one repeating unit).

(3) A cellulose derivative in which repeating units of different substitution positions or different kinds of the substituents in the A) to C) are randomly bonded.

In addition, a part of the cellulose derivative may contain an unsubstituted repeating unit (that is, a repeating unit in which all of R², R³ and R⁶ are a hydrogen atom in Formula (1)).

A) the hydrocarbon group may be any one of an aliphatic group and an aromatic group. When the hydrocarbon group is an aliphatic group, it may be straight, branched or cyclic and may have an unsaturated bond. Examples of the aliphatic group include an alkyl group, a cycloalkyl group, an alkenyl group, an alkynyl group and the like. Examples of the aromatic group include a phenyl group, a naphthyl group, a phenanthryl group, an anthryl group, and the like.

A) the hydrocarbon group is preferably an aliphatic group, more preferably an alkyl group, and even more preferably an alkyl group having 1 to 4 carbon atoms (a lower alkyl group). Specific examples thereof include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a pentyl group, a hexyl group, a heptyl group, a 2-ethylhexyl group, a tert-butyl group, an isoheptyl group and the like, with a methyl group or an ethyl group being preferred.

In the acyl group (—CO—R_(B1)), R_(B1) represents a hydrocarbon group. R_(B1) may be any one of an aliphatic group and an aromatic group. When the hydrocarbon group is an aliphatic group, it may be straight, branched or cyclic and may have an unsaturated bond. Examples of the aliphatic group include an alkyl group, a cycloalkyl group, an alkenyl group, an alkynyl group and the like. Examples of the aromatic group may include a phenyl group, a naphthyl group, a phenanthryl group, an anthryl group, and the like.

R_(B1) is preferably an alkyl group or an aryl group. R_(B1) is more preferably an alkyl group having 1 to 12 carbon atoms or an aryl group, even more preferably an alkyl group having 1 to 12 carbon atoms, further more preferably an alkyl group having 1 to 4 carbon atoms, and most preferably an alkyl group having 1 or 2 carbon atoms (that is, a methyl group or an ethyl group).

Specific examples of the R_(B1) include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a pentyl group, a hexyl group, a heptyl group, a 2-ethylhexyl group, a tert-butyl group, an isoheptyl group, a phenyl group, a naphthyl group and the like. Preferably, R_(B1) is a methyl group, an ethyl group, a propyl group and a phenyl group, and more preferably, R_(B1) is a methyl group, an ethyl group or a propyl group.

In addition, in the alkyleneoxy group (—R_(B2)—O—), an alkylene group moiety (R_(B2)) having 3 carbon atoms may be straight, branched or cyclic, but is preferably straight or branched, and more preferably branched.

Specifically, as the alkyleneoxy group (—R_(B2)—O—), the following structure can be exemplified.

Among the above-mentioned groups, a group represented by the following formula (1) or (2), wherein the alkylene group moiety, is branched is preferred.

A plurality of the alkyleneoxy groups may be contained in the group of B), but a single alkyleneoxy group is preferably contained. When a plurality of the alkyleneoxy groups are contained, a structure of the alkylene group moiety having 3 carbon atoms may be the same or different.

Further, the bonding direction of the alkyleneoxy group to the cellulose derivative is not particularly limited. However, it is preferred that an alkylene group moiety of the alkyleneoxy group is bonded to a side of a cellulose derivative molecule (a side of a glucose ring).

B) the group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—) is preferably a group containing a structure represented by the following formula (3).

In the formula, R_(B1) represents a hydrocarbon group, and R_(B2) represents an alkylene group having 3 carbon atoms.

The definition and preferable range of R_(B1) and R_(B2) in formula (3) are the same as those previously described.

The group of B) may include a plurality of alkyleneoxy groups, or only one group. More specifically, the group of B) may be represented by the following Formula (1′).

In the formula, R_(B1) represents a hydrocarbon group, and R_(B2) represents an alkylene group having 3 carbon atoms. n represents a repeating number, and is a number of 1 or more.

The definition and preferable range of R_(B1) and R_(B2) in formula (1′) are the same as those previously described.

The upper limit of n is not particularly limited and changes depending on the amount of alkyleneoxy groups introduced, and the like. However, the upper limit is, for example, about 10.

Further, in the cellulose derivative, the group containing only one alkyleneoxy group (a group in which n is 1 in formula (1′)) in B) and the group containing two or more alkyleneoxy groups (a group in which n is 1 in Formula (1′)) in B) may be contained by mixture.

In C) the acyl group (—CO—R_(C)), R_(C) represents a hydrocarbon group. As a hydrocarbon group represented by R_(C), one exemplified in the R_(B) may be applied. The preferable range of R_(C) is also the same as that of the R_(B1).

In the cellulose derivative, A) the hydrocarbon group, the hydrocarbon group represented by the R_(B1) and R_(C), and the alkylene group having 3 carbon atoms, represented by R_(B2) may have further substituents, or may be unsubstituted, but is preferably unsubstituted.

In particular, when R_(B1) and R_(C) have further substituents, it is preferred that a substituent which imparts water solubility, for example, a sulfonic acid group, a carboxyl group and the like, is not contained. A cellulose derivative which is water-insoluble and a molding material composed of the cellulose derivative may be obtained by excluding such a group. Further, when the cellulose derivative has a sulfonic acid group, a carboxyl group or the like, it is known that those groups deteriorate the stability of a compound, and it is preferred that the cellulose derivative does not contain these groups because these groups accelerate a thermal decomposition.

When A) the hydrocarbon group, R_(B1), R_(C) and R_(B2) have further substituents in the cellulose derivative, examples of the substituent include a halogen atom (for example, a fluorine atom, a chlorine atom, a bromine atom and an iodine atom), a hydroxyl group, an alkoxy group (the carbon number of an alkyl group moiety is preferably 1 to 5), an alkenyl group and the like. Meanwhile, when A) the hydrocarbon group, R_(B1), R_(C) and R_(B2) are other than an alkyl group, it is possible to have an alkyl group (preferably 1 to 5 carbon atoms) as a substituent.

Further, it is preferred that the cellulose derivative in the present invention has substantially no water-soluble substituent such as a carboxyl group, a sulfonic acid group and salts thereof. The cellulose derivative may have substantially no carboxyl group so as to allow a thermo-molding material to be water-insoluble, thereby improving moldability.

Meanwhile, as used herein, “having substantially no carboxyl group” means to include the case where the cellulose derivative in the present invention has absolutely no carboxyl group, as well as the case where the cellulose derivative in the present invention has a very small amount of a carboxyl group in a range that the cellulose derivative is water-insoluble. For example, when a carboxyl group is contained in cellulose as a raw material cellulose, a cellulose derivative in which the substituent of A) to C) is introduced by using the cellulose may contain a carboxyl group. However, the cellulose derivative is meant to be included in “a cellulose derivative having substantially no carboxyl group”.

The carboxyl group contained in the cellulose derivative of the present invention is included in an amount of preferably 1 mass % or less, and more preferably 0.5 mass % or less, based on the cellulose derivative.

In addition, the cellulose derivative in the present invention is preferably water-insoluble. Here, “water-insoluble” means that the solubility in 100 parts by mass of water (pH 3 to 11) at 25° C. is 5 parts by mass or less.

Specific examples of the cellulose derivative of the present invention include acetoxypropylmethylacetyl cellulose, acetoxypropylethylacetyl cellulose, acetoxypropylpropylacetyl cellulose, acetoxypropylbutylacetyl cellulose, acetoxypropylpentylacetyl cellulose, acetoxypropylhexylacetyl cellulose, acetoxypropylcyclohexylacetyl cellulose, acetoxypropylphenylacetyl cellulose, acetoxypropylnaphthylacetyl cellulose,

propionyloxypropylmethylacetyl cellulose, propionyloxypropylethylacetyl cellulose, propionyloxypropylpropylacetyl cellulose, propionyloxypropylbutylacetyl cellulose, propionyloxypropylpentylacetyl cellulose, propionyloxypropylhexylacetyl cellulose, propionyloxypropylcyclohexylacetyl cellulose, propionyloxypropylphenylacetyl cellulose, propionyloxypropylnaphthylacetyl cellulose,

valerooxypropylmethylvaleroyl cellulose, acetoxypropylpropionyloxypropylmethylacetylpropionyl cellulose, butyryloxypropylmethylacetyl cellulose, acetoxypropylbutyryloxypropylmethylacetylbutyryl cellulose, benzoyloxypropylmethyl cellulosebenzoate and the like.

The positions of substitution of A) the hydrocarbon group, B) the group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—), and C) the acyl group (—CO—R_(C)) in the cellulose derivative and the numbers of each substituent per β-glucose ring unit (the degrees of substitution) are not particularly limited.

For example, the degree of substitution DSa of A) the hydrocarbon group (the number of A) the hydrocarbon groups with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a β-glucose ring in a repeating unit) is preferably 1.0<DSa, and more preferably 1.0<DSa<2.5.

The degree of substitution DSb of B) the group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—) (the number of B) the group containing an acyl group and an alkyleneoxy group with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a cellulose structure of a β-glucose ring in a repeating unit) is preferably 0<DSb, and more preferably 0<DSb<1.0. Since the melting initiation temperature may be lowered in a range of 0<DSb, the thermo-molding may be more easily performed.

The degree of substitution DSc of C) the acyl group (—CO—R_(C)) (the number of C) the acyl groups with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a cellulose structure of a β-glucose ring in a repeating unit) is preferably 0.1<DSc and more preferably 0.1<DSc<2.0.

The mechanical strength, moldability and the like, of the cellulose derivative may be improved by setting the degree of substitution in the aforementioned range.

Further, the number of unsubstituted hydroxyl groups existing in the cellulose derivative is not particularly limited, either. The degree of substitution DSh of hydrogen atoms (the ratio at which hydroxyl groups at the 2-, 3- and 6-positions in a repeating unit are unsubstituted) may be in a range of 0 to 1.5, and preferably 0 to 0.6. The fluidity of a thermo-molding material may be enhanced or foaming due to water absorption of the thermo-molding material at the time of acceleration and molding of thermal decomposition, and the like, may be suppressed by setting the DSh to 0.6 or less.

In addition, the cellulose derivative in the present invention may have a substituent other than A) the hydrocarbon group, B) the group containing an acyl group (—CO—R_(B1)) and an alkyleneoxy group (—R_(B2)—O—), and C) the acyl group (—CO—R_(C)). Examples of the substituent which the cellulose derivative may have include a hydroxypropyl group, a hydroxypropoxypropyl group and hydroxypropoxypropoxypropyl group. Therefore, although the sum of each degree of substitution of all the substituents that the cellulose derivative has is 3, the (DSa+DSb+DSc+DSh) is 3 or less.

Furthermore, the amount of an alkyleneoxy group introduced in the group of B) is represented by a molar degree of substitution (MS: the number of moles of substituents introduced per glucose residue) (Cellulose Dictionary P142, edited by Cellulose Society of Japan). The molar degree of substitution MS of the alkyleneoxy group is preferably 0<MS, more preferably 0<MS≦1.5, and even more preferably 0<MS<1.0. Since MS is 1.5 or less (MS≦1.5), heat resistance-moldability and the like, may be improved, and thus, a cellulose derivative appropriate for a thermo-molding material may be obtained.

In the molecular weight of the cellulose derivative, the number average molecular weight (Mn) is preferably in a range of 5×10³ to 1000×10³, more preferably in a range of 10×10³ to 500×10³, and most preferably in a range of 10×10³ to 200×10³. Further, the weight average molecular weight (Mw) thereof is preferably in a range of 7×10³ to 10,000×10³, more preferably in a range of 15×10³ to 5,000×10³, and most preferably in a range of 100×10³ to 3,000×10³. The moldability, mechanical strength and the like, of a molded body may be improved by setting the average molecular weight in that range.

The molecular weight distribution (MWD) is preferably in a range of 1.1 to 10.0 and more preferably in a range of 1.5 to 8.0. Moldability and the like, may be improved by setting the molecular weight distribution in that range.

In the present invention, the number average molecular weight (Mn), weight average molecular weight (Mw) and molecular weight distribution (MWD) may be measured by using a gel permeation chromatography (GPC). Specifically, N-methylpyrrolidone is used as a solvent and a polystyrene gel is used, and the molecular weight may be obtained by using a reduced molecular weight calibration curve previously prepared from a standard monodispersion polystyrene constitution curve.

In addition, among the above-described cellulose derivatives, particularly the cellulose derivatives of the following (1) and (2) are novel compounds, and have excellent thermoplasticity and mechanical strength (particularly, toughness), which are particularly useful as a thermo-molding material.

(1) A water-insoluble cellulose derivative containing a1) an ethyl group, b1) a group containing an acyl group: —CO—Rb1 (Rb1 represents a hydrocarbon group) and an alkyleneoxy group: —Rb2-O— (Rb2 represents an alkylene group having 3 carbon atoms), and c1) an acyl group: —CO—Rc (Rc represents a hydrocarbon group).

(2) A cellulose derivative containing a2) a methyl group and b2) a group containing an acyl group: —CO—Rb1 (Rb1 represents a hydrocarbon group) and an alkyleneoxy group: —Rb2-O— (Rb2 represents an alkylene group having 3 carbon atoms), and c2) an acyl group: —CO—Rc (Rc represents a hydrocarbon group), wherein the cellulose derivative has a degree of substitution of a) the methyl group of 1.1 or more, and a molar degree of substitution (MS) of the alkyleneoxy group of 1.5 or less, and is water-insoluble.

As a hydrocarbon group represented by Rb1 and Rc, one exemplified in the R_(B1) may be applied. The preferable range of Rb1 and Rc is also the same as that of the R_(B1). Further, as an alkylene group having 3 carbon atoms, represented by Rb2, one exemplified in the R_(B2) may be applied. The preferable range of Rb2 is also the same as that of the R_(B2).

In an embodiment of (1), the degree of substitution and the like, are not particularly limited, and the above-described range may be applied to a preferable range of the degree of substitution.

In an embodiment of (2), the degree of substitution of a2) the methyl group is preferably 1.1 or more, and 2.5 or less, and more preferably 1.1 or more, and 2.0 or less. In addition, the molar degree of substitution (MS) of the alkyleneoxy group is preferably more than 0 and 1.5 or less, and more preferably 0.1 or more, and 1.2 or less. Other degrees of substitution are not particularly limited, and the above-described range may be applied as a preferable range.

Furthermore, in the embodiments of (1) and (2), it is preferred that the cellulose derivative has substantially no carboxyl group.

2. Preparation Method of Cellulose Derivative

A preparation method of the cellulose derivative in the present invention is not particularly limited, and the cellulose derivative of the present invention may be prepared by using cellulose as a raw material and subjecting the cellulose to etherification and esterification. Any raw material of cellulose may be used, including, for example, cotton, linter, pulp and the like.

A preferred embodiment of the preparation method of the cellulose derivative in the present invention is performed by a method including a process of allowing hydroxypropylcellulose ether having a hydrocarbon group and a hydroxypropyl group to react with acid chloride or acid anhydride to perform esterification (acylation).

In addition, as another embodiment, methods including processes of etherification of cellulose ether such as, for example, methyl cellulose and ethyl cellulose with propyleneoxide and the like, or etherification of allowing alkyl chloride such as methyl chloride and ethyl chloride/alkylene oxide having 3 carbon atoms to react with cellulose and then follow by reaction with acid chloride or acid anhydride to perform esterification may be included.

As a method of reacting the acid chloride, for example, a method described in Cellulose 10; 283-296, 2003 may be used.

The cellulose derivative of the present invention may be obtained through esterification of hydroxypropylalkyl cellulose. Since the esterification occurs for hydroxyl groups of hydroxypropyl and hydroxyl groups of cellulose, a plural kinds of esterified hydroxypropyl groups and esterified celluloses may be obtained when using a plurality of esterifying agents (anhydride/acid chloride) to perform a reaction.

Specific examples of cellulose ether having a hydrocarbon group and a hydroxypropyl group include hydroxypropylmethyl cellulose, hydroxypropylethyl cellulose, hydroxypropylpropyl cellulose, hydroxypropylallyl cellulose, hydroxypropylbenzyl cellulose and the like. Preferably, the examples thereof are hydroxypropylmethyl cellulose and hydroxypropylethyl cellulose.

In the case of hydroxypropylmethyl cellulose, those commercially available may be used. In commercially available products, there are four kinds of degrees of substitution, and there are types corresponding to hypromellose 1828, 2208, 2906 and 2910 as described in Japanese Pharmacopoeia, US Pharmacopoeia and European Pharmacopoeia. Any one may be used. Furthermore, for a type having each degree of substitution, a viscosity level is represented by a viscosity value of a 2% aqueous solution at 20° C., and the viscosity value is about 1 to 200,000. Generally, those types having a high viscosity level have higher molecular weights (Mn and Mw) than those having a low viscosity level. The molecular weight of a cellulose derivative produced may be controlled by changing the viscosity level to be used.

As the acid chloride, carboxylic acid chloride corresponding to the acyl group included in the B) and C) the acyl group may be used. Examples of carboxyl acid chloride include acetyl chloride, propionyl chloride, butyryl chloride, isobutyryl chloride, pentanoyl chloride, 2-methylbutanoyl chloride, 3-methylbutanoyl chloride, pyvaloyl chloride, hexanoyl chloride, 2-methylpentanoyl chloride, 3-methylpentanoyl chloride, 4-methylpentanolyl chloride, 2,2-dimethylbutanoyl chloride, 2,3-dimethylbutanoyl chloride, 3,3-dimethylbutanoyl chloride, 2-ethylbutanoyl chloride, heptanoyl chloride, 2-methylhexanoyl chloride, 3-methylhexanoyl chloride, 4-methylhexanoyl chloride, 5-methylhexanolyl chloride, 2,2-dimethylpentanoyl chloride, 2,3-dimethylpentanoyl chloride, 3,3-dimethylpentanoyl chloride, 2-ethylpentanoyl chloride, cyclohexanoyl chloride, octanoyl chloride, 2-methylheptanoyl chloride, 3-methylheptanoyl chloride, 4-methylheptanoyl chloride, 5-methylheptanoyl chloride, 6-methylheptanoyl chloride, 2,2-dimethylhexanolyl chloride, 2,3-dimethylhexanolyl chloride, 3,3-dimethylhexanolyl chloride, 2-ethylhexanoyl chloride, 2-propylpentanoyl chloride, nonanoyl chloride, 2-methyloctanoyl chloride, 3-methyloctanoyl chloride, 4-methyloctanoyl chloride, 5-methyloctanoyl chloride, 6-methyloctanoyl chloride, 2,2-dimethylheptanoyl chloride, 2,3-dimethylheptanoyl chloride, 3,3-dimethylheptanoyl chloride, 2-ethylheptanoyl chloride, 2-propylhexanoyl chloride, 2-butylpentanoyl chloride, decanoyl chloride, 2-methylnonanoyl chloride, 3-methylnonanoyl chloride, 4-methylnonanoyl chloride, 5-methylnonanoyl chloride, 6-methylnonanoyl chloride, 7-methylnonanoyl chloride, 2,2-dimethyloctanoyl chloride, 2,3-dimethyloctanoyl chloride, 3,3-dimethyloctanoyl chloride, 2-ethyloctanoyl chloride, 2-propylheptanoyl chloride, 2-butylhexanoyl chloride and the like.

As the acid anhydride, for example, carboxylic acid anhydride corresponding to the acyl group included in B), and C) the acyl group may be used. Examples of the carboxylic acid anhydride include acetic anhydride, propionic anhydride, butyric anhydride, valeric anhydride, hexanoic anhydride, heptanoic anhydride, octanoic anhydride, 2-ethylhexanoic anhydride, nonanoic anhydride and the like.

Meanwhile, as described above, it is preferred that the cellulose derivative in the present invention does not have carboxylic acid as a substituent, and thus, it is preferred not to use a compound having carboxylic acid produced by reacting with cellulose, such as dicarboxylic acid such as anhydrous phthalic acid and anhydrous maleic acid.

As a catalyst, an acid may be used. Examples of preferred acids include sulfuric acid, methanesulfonic acid, p-toluene sulfonic acid, perchloric acid, phosphoric acid, trifluoroacetic acid, trichloroacetic acid and the like. More preferably, the examples thereof include sulfuric acid and methanesulfonic acid. Further, bisulfate may be used, and examples thereof include lithium bisulfate, sodium bisulfate and potassium bisulfate. In addition, a solid acid catalyst may be used, and examples thereof include polymer solid acid catalysts such as an ion exchange resin, solid acid catalysts based on inorganic oxides, which is exemplified by zeolite, and carbon-type solid acid catalysts such as those used in Japanese Patent Application Laid-Open No. 2009-67730. Furthermore, a Lewis acid catalyst may be used, and examples thereof include titanic acid ester catalysts such as those used in U.S. Pat. No. 2,976,277, and zinc chloride.

As a catalyst, a base may be used. Examples thereof include pyridines, alkali metal salts of acetic acid such as sodium acetate, dimethylaminopyridine, and anilines.

There is also a reaction system in which the esterification reaction proceeds even though a catalyst is not used. Examples thereof include reactions systems using N,N-dimethylacetamide as a solvent, and acetyl chloride or propionyl chloride as an acetylating agent.

As a solvent, a general organic solvent may be used. Among them, carboxylic acid-based or carboxamide-based solvents are preferred. As a carboxylic acid, carboxylic acid corresponding to the acyl group included in B) and the acyl group included in C) may be used. When carboxylic acid is used, ethyl acetate or acetonitrile may be used in combination. As a carboxamide-based solvent, there are those used in Japanese Patent Application Laid-Open No. 10-5117129 or U.S. Pat. No. 2,705,710, and examples thereof include N,N-dimethylacetamide. Further, dimethyl sulfoxide including lithium chloride used in Japanese Patent Application Laid-Open No. 2003-41052 may be used. In addition, a halogenating solvent may be used, and is preferably dichloromethane. Furthermore, pyridine may be used, which may be used as a base. In addition, as used in Japanese Patent Application Laid-Open No. Hei 9-157301, acid chloride used as an esterifying agent may be used as a solvent.

A cellulose derivative (including cellulose) used as a raw material is produced from biomass resources such as cotton linters and wood pulp. Raw materials other than cellulose derivatives may be produced from biomass resources. Examples thereof include acetic acid or anhydrous acetic acid produced by a fermentation method from ethanol produced from cellulose-based biomass or starch-based biomass.

As a pre-treatment, as in Japanese Patent No. 2754066, carboxylic acid or acetic acid including a small amount of an acid catalyst may be added to a cellulose derivative as a raw material and may be mixed.

Prior to use, the cellulose derivative as a raw material may be dried to reduce moisture contained in the cellulose derivative. The moisture contained is responsible for a side reaction of reacting with anhydrous acetic acid, and thus, it is possible to reduce the amount of anhydrous acetic acid used by reducing the moisture contained.

As in Japanese Patent No. 2754066, the rate of the esterification reaction may be controlled by adding the catalyst in parts, or changing the addition rate or combining these. The esterification reaction is an extremely exothermic reaction and the reaction solution also becomes highly viscous, and thus, the esterification reaction is effective when it is difficult to remove heat.

As in Japanese Patent Application Laid-Open No. Sho 60-139701, a reaction product may be concentrated by condensing vapor generated by reducing pressure in the reaction system for the whole period of the esterification reaction or for some periods including the initial phase to release the vapor out of the reaction system. In this method, the heat of reaction generated by the esterification reaction may be taken away by the latent heat of vaporization of a volatile solvent to remove heat.

As in Japanese Patent Application Laid-Open No. 2000-511588, the esterification reaction may be performed in multiple steps. For example, cellulose may be reacted with a first acetylating agent as a first step in the presence of a base catalyst, followed by reaction as a second step with a second acetylating agent in the presence of an acid catalyst.

If the temperature of the esterification reaction is high, the rate of the esterification reaction may become rapid, and thus, the reaction time may be reduced. However, the molecular weight is likely to be reduced by the depolymerization reaction. If the temperature is low, the esterification reaction is delayed. It is preferred that the reaction temperature and time are controlled according to the structure of a desired cellulose derivative and desired molecular weights (Mn and Mw).

When the esterification is performed, the reaction may be performed by irradiating ultrasonic waves as in International Publication No. WO 2001/070820.

In the esterification reaction, the mixture in the reactor progressively changes from the solid-liquid state to a dope-type as the reaction proceeds, and thus, the doping viscosity in the reaction system is increased to a very high value. As described in Japanese Patent Publication No. Hei 2-5761, the doping viscosity is further increased in a method of performing the esterification reaction under reduced pressure conditions while gas-phase components in the reaction system are being distilled away out of the reaction system. As shown in these, when the doping viscosity is increased to a very high value, it is preferred to use a biaxial kneader as an esterification reactor. In addition, the doping viscosity may be lowered to use a general-purpose glass-lined reaction vessel and the like, by increasing the amount of carboxylic acid in the solvent or using other organic solvents in combination to decrease the concentration of the reaction solution.

After the esterification process is completed, a base (generally in the form of an aqueous solution), or water (alcohol may also be used) is added thereto to degrade unreacted anhydrous acetic acid and stop the reaction. An acid catalyst is neutralized when a base is added, while the acid catalyst is not neutralized when water is added. Although it is generally preferred to neutralize the catalyst, the catalyst may not be neutralized. It is better to neutralize the catalyst, for example, when the thermal stability of a synthesized polymer is reduced by effects of bonding sulfuric acid bonded to the cellulose derivative. Further, a method of reducing the amount of bonding sulfuric acid may include a method for neutralizing the bonding sulfuric acid not at once, but step by step while maintaining liquid property that is easily degradable, by means of adding a base continuously, as described in Japanese Patent Application Laid-Open No. 2006-89574. What is used as a neutralizing agent is not particularly limited so long as the agent is a base. However, preferable examples thereof include alkali metal compounds or alkaline earth metal compounds, and specific examples thereof include sodium acetate, potassium acetate, calcium acetate, magnesium acetate, calcium hydroxide, magnesium hydroxide and the like.

A method for separating a desired cellulose derivative is not particularly limited, and methods such as, for example, precipitation, filtration, washing, drying, extraction, concentration and column chromatography may be used either alone or in combination of two or more species appropriately. However, from the standpoint of manipulability, purification efficiency and the like, it is preferred to use a method for separating the cellulose derivative by precipitation (reprecipitation) manipulation. The precipitation manipulation is performed by mixing a solution containing the cellulose derivative with a poor solvent in a manner of introducing the reaction solution containing the cellulose derivative into the poor solution of the cellulose derivative, or introducing the poor solution into the solution containing the cellulose derivative.

As a poor solvent of a desired cellulose derivative, a solvent which is low in solubility in the cellulose derivative may be used, and examples thereof include diluted acetic acid, water, alcohols and the like. Preferably, the poor solvent is diluted acetic acid or water.

A method for solid-liquid separation of the obtained precipitate is not particularly limited, and methods such as filtration and sedimentation may be used. Preferably, the method is filtration, and may use various dehydrators using depressurization, pressurization, gravitational force, compression, centrifugation and the like. Examples thereof include a vacuum dehydrator, a pressurized dehydrator, a belt press, a centrifugal filtration dehydrator, a vibrating screen, a roller press, a belt screen and the like.

Acetic acid, acids used as acid catalysts, solvents, and dissociated metal components are frequently removed from the separated precipitate by washing, for example, with water. Particularly, it is preferred to remove acetic acid and acids used as acid catalysts because they are responsible for molecular weight reduction of a resin during molding and accordingly, degradation in physical performance.

A neutralizing agent may be added during washing. What is used as a neutralizing agent is not particularly limited so long as the agent is a base. Preferable examples thereof include alkali metal compounds or alkaline earth metal compounds, and specific examples thereof include sodium acetate, potassium acetate, calcium acetate, magnesium acetate, calcium hydroxide, magnesium hydroxide and the like. Further, as in Japanese Patent Publication No. Hei 6-67961, a buffer solution may be used in the washing.

A drying method is not particularly limited, and drying may be performed under conditions of blow drying, depressurization and the like, or various dehydrators may be used.

Other detailed preparation conditions may be set according to a general method. For example, see a method described on pages 131 to 164 of “Dictionary of Cellulose” (Asakura Publishing Co., Ltd., 2000).

3. Thermo-Molding Material and Molded Body

A thermo-molding material of the present invention contains the above-described cellulose derivative, and may contain other additives if necessary.

The content of the component contained in the thermo-molding material is not particularly limited. The content of the cellulose derivative is preferably 75 mass % or more, more preferably 80 mass % or more, and even more preferably 80 to 100 mass %.

The thermo-molding material of the present invention may include various additives such as a filler and a flame retardant, if necessary, in addition to the cellulose derivative of the present invention.

The thermo-molding material of the present invention may contain a filler (reinforcing material). By containing a filler, mechanical properties of a molded body formed by the thermo-molding material may be reinforced.

As a filler, a known matter may be used. The shape of the filler may be any one of a fiber type, a plate type, a particle type and a powder type. Further, the filler may be an inorganic material or an organic material.

Specific examples of the inorganic filler include a fiber type inorganic filler such as glass fiber, carbon fiber, graphite fiber, metal fiber, potassium titanate whisker, aluminum borate whisker, magnesium-based whisker, silicon-based whisker, wollastonite, sepiolite, slag fiber, xonotlite, ellestadite, gypsum fiber, silica fiber, silica-alumina fiber, zirconia fiber, boron nitride fiber, silicon nitride fiber and boron fiber; or a plate type or particle type inorganic filler such as glass flake, non-swelling mica, carbon black, graphite, metal foil, ceramic bead, talc, clay, mica, sericite, zeolite, bentonite, dolomite, kaolin, fine silicate, feldspar sand, potassium titanate, shirasu balloon, calcium carbonate, magnesium carbonate, barium sulfate, calcium oxide, aluminum oxide, titanium oxide, magnesium oxide, aluminum silicate, silicon oxide, aluminum hydroxide, magnesium hydroxide, gypsum, novaculite, dawsonite and white clay.

Examples of the organic filler include synthetic fiber such as polyester fiber, nylon fiber, acryl fiber, regenerated cellulose fiber and acetate fiber, natural fiber such as kenaf, ramie, cotton, jute, hemp, sisal, Manila hemp, flax, linen, silk and wool, a fiber type organic filler obtained from microcrystalline cellulose, sugar cane, wood pulp, tissues and waste paper, or a particle type organic filler such as an organic pigment.

When the thermo-molding material contains a filler, the content thereof is not limited, but the content may be generally 30 parts by mass or less, and preferably 5 to 10 parts by mass, based on 100 parts by mass of the cellulose derivative.

The thermo-molding material of the present invention may contain a flame retardant. By this, a flame retardant effect may be improved, which decreases or suppresses a combustion speed.

The flame retardant is not particularly limited, and may be one commercially available. For example, a bromine-based flame retardant, a chlorine-based flame retardant, a phosphorus-containing flame retardant, a silicon-containing flame retardant, a nitrogen compound-based flame retardant, an inorganic-based flame retardant, and the like, may be exemplified. Among them, the phosphorus-containing flame retardant and silicon-containing flame retardant are preferable, because corrosion of processing machines or molds, or deterioration of operation environments are not caused by the halogenated hydrogen generated by thermal decomposition when compositing with the resin or molding processing, and also, it is unlikely that the environment would be negatively affected by harmful materials such as dioxins generated by dispersing or decomposing halogen gas during incineration and discarding.

The phosphorus-containing flame retardant is not particularly limited, and may be commercially available. For example, an organic phosphorus-based compound such as phosphate ester, condensed phosphate ester and polyphosphate may be used.

Specific examples of phosphate ester include trimethyl phosphate, triethyl phosphate, tributyl phosphate, tri(2-ethylhexyl) phosphate, tributoxyethyl phosphate, triphenyl phosphate, tricresyl phosphate, trixylenyl phosphate, tris(isopropylphenyl) phosphate, tris(phenylphenyl) phosphate, trinaphthyl phosphate, cresvldiphenyl phosphate, xylenyldiphenyl phosphate, diphenyl(2-ethylhexyl)phosphate, di(isopropylphenyl) phenylphosphate, monoisodecyl phosphate, 2-acryloyloxyethyl acid phosphate, 2-methacryloyloxyethyl acid phosphate, diphenyl-2-acryloyloxyethyl phosphate, diphenyl-2-methacryloyloxyethyl phosphate, melamine phosphate, dimelamine phosphate, melamine pyrrophosphate, triphenyl phosphine oxide, tricresyl phosphine oxide, diphenyl methane phosphonate, diethyl phenylphosphonate and the like.

Condensed phosphate ester may include, for example, aromatic condensed phosphate ester such as resorcinol polyphenylphosphate, resorcinol poly(di-2,6-xylyl)phosphate, bisphenol A polycresylphosphate, hydroquinone poly(2,6-xylyl)phosphate, and a condensate thereof.

Further, polyphosphate formed of salts of phosphoric acid, polyphosphoric acid with a metal of Groups 1 to 14 of the periodic table, ammonia, aliphatic amine and aromatic amine may be exemplified. The representative salt of polyphosphate may include a metal salt such as lithium salt, sodium salt, calcium salt, barium salt, iron(II) salt, iron(III) salt, aluminum salt, and the like, aliphatic amine salt such as methylamine salt, ethylamine salt, diethylamine salt, triethylamine salt, ethylenediamine salt and piperazine salt, and aromatic amine salt such as pyridine salt and triazine.

In addition to the above, halogen-containing phosphate ester such as trischloroethylphosphate, trisdichloropropylphosphate, tris(β-chloropropyl)phosphate), a phosphagen compound having a structure in which a phosphorus atom and a nitrogen atom are linked by a double bond, and phosphate ester amide may be exemplified.

The phosphorus-containing flame retardants may be used either alone or in combination of two or more species.

The silicon-containing flame retardant may include an organic silicon compound having a two or three dimensional structure, polydimethylsiloxane, a compound in which a methyl group of a side chain or a terminal of polydimethylsiloxane is substituted or modified by a hydrogen atom, a substituted or unsubstituted aliphatic hydrocarbon group, and an aromatic hydrocarbon group, so-called silicone oil or modified silicone oil.

Examples of the substituted or unsubstituted aliphatic hydrocarbon group and aromatic hydrocarbon group include an alkyl group, a cycloalkyl group, a phenyl group, a benzyl group, an amino group, an epoxy group, a polyether group, a carboxyl group, a mercapto group, a chloroalkyl group, an alkyl higher alcohol ester group, an alcohol group, an aralkyl group, a vinyl group or a trifluoromethyl group.

The silicon-containing flame retardants may be used either alone or in combination of two or more species.

Further, examples of a flame retardant other than the phosphorus-containing flame retardant or silicon-containing flame retardant include an inorganic-based flame retardant such as magnesium hydroxide, aluminum hydroxide, antimony trioxide, antimony pentoxide, soda antimonate, zinc hydroxystannate, zinc stannate, metastannic acid, tin oxide, tin oxide salt, zinc sulfate, zinc oxide, ferrous oxide, ferric oxide, stannous oxide, stannic oxide, zinc borate, ammonium borate, ammonium octamolybdate, metal salt of tungsten acid, complex oxide of tungsten and metalloid, ammonium sulfamate, ammonium bromide, a zirconium-based compound, a guanidine-based compound, a fluorine-based compound, graphite and swelling graphite. The other flame retardants may be used either alone or in combination of two or more species.

When the thermo-molding material of the present invention contains a flame retardant, the content thereof is not limited, but the content may be generally 30 parts by mass or less, and preferably 2 to 10 parts by mass, based on 100 parts by mass of the cellulose derivative. By setting the content to the above range, it is possible to improve impact resistance and brittleness, or to suppress occurrence of pellet blocking.

The thermo-molding material of the present invention may include other components for the purpose of further improving various properties such as moldability, flame retardancy, and the like, within a scope in which the object of the present invention is not hindered, in addition to the cellulose derivative, filler and flame retardant.

Examples of the other components include a polymer other than the cellulose derivative, a plasticizer, a stabilizer (antioxidant, UV absorbing agent, and the like), a release agent (fatty acid, fatty acid metal salt, oxy fatty acid, fatty acid ester, aliphatic partially saponificated ester, paraffin, low molecular weight polyolefin, fatty acid amide, alkylene-bis fatty acid amide, aliphatic ketone, fatty acid lower alcohol ester, fatty acid polyvalent alcohol ester, fatty acid polyglycol ester and modified silicone), an antistatic agent, a flame retardant formulation, a processing formulation, a drip inhibitor, an antimicrobial, an anti-fungal agent and the like. Further, a coloring agent including a dye or pigment may be added.

As the polymer other than the cellulose derivative, a thermoplastic polymer or a thermosetting polymer may be used, but the thermoplastic polymer is preferable from the standpoint of moldability. Specific examples of the polymer other than the cellulose derivative include polyolefins such as low density polyethylene, straight chain type low density polyethylene, high density polyethylene, polypropylene, ethylene-propylene copolymer, ethylene-propylene-non-conjugated diene copolymer, ethylene-butene-1 copolymer, polypropylene homopolymer, polypropylene copolymer (ethylene-propylene block copolymer, and the like), polybutene-1 and poly-4-methylpentene-1, polyesters such as polybutylene terephthalate, polyethylene terephthalate and other aromatic polyester, polyamides such as nylon 6, nylon 46, nylon 66, nylon 610, nylon 612, nylon 6T and nylon 12, polystyrene, high impact polystyrene, polyacetal (including homopolymer and copolymer), polyurethane, aromatic and aliphatic polyketone, polyphenylene sulfide, polyether ether ketone, thermoplastic starch resin, acryl resins such as polymethyl methacrylate or methacrylic ester-acrylic ester copolymer, AS resin (acrylonitrilestyrene copolymer), ABS resin, AES resin (ethylene-based rubber reinforced AS resin), ACS resin(chlorinated polyethylene reinforced AS resin), ASA resin (acryl-based rubber reinforced AS resin), polyvinyl chloride, polyvinylidene chloride, vinyl ester-based resin, maleic anhydride-styrene copolymer, MS resin (methyl methacrylate-styrene copolymer), polycarbonate, polyarylate, polysulfone, polyether sulfone, phenoxy resin, polyphenylene ether, modified polyphenylene ether, thermoplastic polyimides such as polyether imide, fluorine-based polymers such as polytetrafluoroethylene, tetrafluoroethylene-hexafluoropropylene copolymer, tetrafluoroethylene-ethylene copolymer, tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer, polychlorotrifluoroethylene, polyvinylidene fluoride and tetrafluoroethylene-hexafluoropropylene-perfluoroalkyl vinyl ether copolymer, cellulose acetate, polyvinyl alcohol, unsaturated polyester, melamine resin, phenol resin, urea resin, polyimide, and the like. Further, there may be various thermoplastic elastomers such as various acryl rubber, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer and alkali metal salt thereof (so-called ionomer), ethylene-alkylester acrylate copolymer (for example, ethylene-ethyl acrylate copolymer and ethylene-butyl acrylate copolymer), diene-based rubber (for example, 1,4-polybutadiene, 1,2-polybutadiene, polyisoprene and polychloroprene), a copolymer of diene and vinyl monomer (for example, styrene-butadiene random copolymer, styrene-butadiene block copolymer, styrene-butadiene-styrene block copolymer, styrene-isoprene random copolymer, styrene-isoprene block copolymer, styrene-isoprene-styrene block copolymer, a copolymer in which styrene is graft copolymerized with polybutadiene, and butadiene-acrylonitrile copolymer), polyisobutylene, copolymer of isobutylene and butadiene or isoprene, butyl rubber, natural rubber, thiokol rubber, polysulfide rubber, acryl rubber, nitrile rubber, polyether rubber, epichlorohydrin rubber, fluorine rubber, silicone rubber, other polyurethanes or polyesters, polyamides.

In addition, a polymer having various degrees of crosslinking, a polymer having various microstructures, for example, a cis structure and a trans structure, a polymer having a vinyl group, a polymer having various average particle diameters, a multilayered structure polymer that is called a core-shell rubber constituted by a core layer, one or more shell layers covering the core layer and the adjacent layers formed of different polymers and core-shell rubber containing a silicon compound may be used.

These polymers may be used either alone or in combination of two or more species.

When the thermo-molding material of the present invention contains a polymer other than the cellulose derivative, the content thereof is preferably 30 parts by mass or less and more preferably 2 parts to 10 parts by mass, based on 100 parts by mass of the cellulose derivative.

The thermo-molding material of the present invention may contain a plasticizer. Therefore, flame retardancy and moldability may be further improved. As the plasticizer, a matter that is commercially used in molding of the polymer may be used. For example, there may be a polyester-based plasticizer, a glycerin-based plasticizer, a polyvalent carboxylic acid ester-based plasticizer, a polyalkyleneglycol-based plasticizer and an epoxy-based plasticizer.

Specific examples of the polyester-based plasticizer include polyester that is formed of an acid component such as adipic acid, sebacic acid, terephthalic acid, isophthalic acid, naphthalene dicarboxylic acid, diphenyldicarboxylic acid and rosin, and a diol component such as propyleneglycol, 1,3-butanediol, 1,4-butanediol, 1,6-hexanediol, ethyleneglycol and diethyleneglycol, or polyester that is formed of hydroxycarboxylic acids such as polycaprolactone. These polyesters may be terminally capped with a monofunctional carboxylic acid or monofunctional alcohol, or may be terminally capped with an epoxy compound and the like.

Specific examples of the glycerin-based plasticizer include glycerin monoacetomonolaurate, glycerin diacetomonolaurate, glycerin monoacetomonostearate, glycerin diacetomonooleate and glycerin monoacetomonomontanate.

Specific examples of the polyvalent carboxylic acid-based plasticizer include phthalic esters such as dimethyl phthalate, diethyl phthalate, dibutyl phthalate, dioctyl phthalate, diheptyl phthalate, dibenzyl phthalate and butylbenzyl phthalate, trimellitic esters such as tributyl trimellitate, trioctyl trimellitate and trihexyl trimellitate, adipic esters such as diisodecyl adipate, n-octyl-n-decyl adipate, methyl diglycol butyldiglycol adipate, benzylmethyldiglycol adipate and benzylbutyldiglycol adipate, citric esters such as triethyl acetylcitrate and tributyl acetylcitrate, azelaic esters such as di-2-ethylhexyl azelate, dibutyl sebacate and di-2-ethylhexyl sebacate.

Specific examples of the polyalkyleneglycol-based plasticizer include polyalkylene glycols such as polyethylene glycol, polypropylene glycol, poly(ethylene oxide-propylene oxide) block and/or random copolymer, polytetramethylene glycol, ethylene oxide addition polymers of bisphenols, propylene oxide addition polymers of bisphenols, and tetrahydrofuran addition polymer of bisphenols, or a terminal-epoxy modified compound thereof, a terminal-ester modified compound thereof and a terminal-ether modified compound thereof.

The epoxy-based plasticizer generally represents the epoxytriglycerides formed of alkyl epoxystearate and soybean oil, but in addition to this, a so-called epoxy resin mainly having bisphenol A and epichlorohydrin as a raw material may be also used.

Specific examples of the other plasticizers may include benzoic esters of aliphatic polyols such as neopentyl glycol dibenzoate, diethylene glycol dibenzoate and triethylene glycol di-2-ethylbutylate, fatty acid amides such as stearic amide, aliphatic carboxylic esters such as butyl oleate, oxylic esters such as methyl acetylricinoleate and butyl acetylricinoleate, pentaerythritol, various sorbitols, and the like.

When the thermo-molding material of the present invention contains a plasticizer, the content thereof is generally 5 parts by mass or less, preferably 0.005 parts to 5 parts by mass and more preferably 0.01 parts to 1 part by mass, based on 100 parts by mass of the cellulose derivative.

The molded body of the present invention is obtained by molding the thermo-molding material including the cellulose derivative. More specifically, the molded body is obtained by a manufacturing method including a process for heating the cellulose derivative, or the thermo-molding material including the cellulose derivative and, if necessary, various additives and molding it by various molding methods.

The molding method may include, for example, injection molding, extrusion molding, blow molding and the like.

The heating temperature is generally 160° C. to 300° C., and preferably 180° C. to 260° C.

A use of the molded body of the present invention is not particularly limited, but may include, for example, interior or exterior parts of electric and electronic devices (devices for home appliances, OA media related devices, optical devices, communication devices and the like), and materials for automobiles, machinery parts, and housing and construction. Among them, from the standpoint of excellent heat resistance, impact resistance and a low load to the environment, for example, the molded body may be suitably used as exterior parts (particularly, case) for electric and electronic devices such as photocopiers, printers, personal computers and televisions.

EXAMPLE

Although the present invention will be described in detail with reference to the following Examples and Comparative Examples, the scope of the present invention is not limited to the following Examples.

Synthetic Example 1 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-1)

30 g of hydroxypropylmethyl cellulose (trade name: Marpolose 60 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-1) and 2,250 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, 84 mL of acetyl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature. The reaction solution was introduced into 10 L of water while vigorously stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed three times with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-1) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (33.7 g).

Synthetic Example 2 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-2)

60 g of hydroxypropylmethyl cellulose (trade name: Marpolose 65 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-2) and 2,100 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, 124 mL of acetyl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature. The reaction solution was introduced into 10 L of water while vigorously stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed three times with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-2) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (73.2 g).

Synthetic Example 3 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-3)

60 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3) and 2,100 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, 168 mL of acetyl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature. The reaction solution was introduced into 10 L of water while vigorously stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed three times with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-3) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (78.7 g).

Synthetic Example 4 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-4)

30 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3) and 1,500 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, 20.6 mL of acetyl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature. The reaction solution was introduced into 10 L of water while vigorously stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed three times with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-4) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (34.0 g).

Synthetic Example 5 Synthesis of Propionyloxypropylmethylpropionyl Cellulose (C-5)

60 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3) and 2,100 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, 192 mL of propionyl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature. The reaction solution was introduced into 10 L of water while vigorously stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed three times with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-5) (propionyloxypropylmethylpropionyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (84.5 g).

Synthesis Example 6 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-6)

60 g of hydroxypropylmethyl cellulose (trade name: Metolose 90SH-100; manufactured by Shin-Etsu Chemical Co., Ltd.; H-4) and 2,100 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, 101 mL of acetyl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature. The reaction solution was introduced into 10 L of water while vigorously stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed three times with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-6) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (79.4 g).

Synthetic Example 7 Synthesis of Butyryloxypropylmethylbutyryl Cellulose (C-7)

60 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3) and 2,100 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, 147 mL of butyryl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature. 100 mL of methanol and 800 ml of water were added dropwise, followed by introduction of a reaction solution into 10 L of water while vigorously stirring. The white solid was separated by suction filtration, and washed three times with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-7) (butyryloxypropylmethylbutyryl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (75.1 g).

Synthetic Example 8 Synthesis of acetoxypropylpropionyloxypropylmethylacetylpropionyl Cellulose (C-8)

60 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3) and 2,100 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, a mixture solution of 66.4 mL of acetyl chloride and 81.2 mL of propionyl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then, the reaction system was cooled to room temperature and left to stand overnight. 100 mL of methanol and 800 mL of water were added dropwise, followed by introduction of a reaction solution into 10 L of water while vigorously stirring. The white solid was separated by suction filtration, and washed three times with large quantities of water. The white solid was dissolved in methanol, and a white solid obtained by dropping the resulting solution into water was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-8) (acetoxypropylpropionyloxypropylmethylacetylpropionyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (77.1 g).

Synthetic Example 9 Synthesis of acetoxypropylpropionyloxypropylmethylacetylpropionyl Cellulose (C-9)

60 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3) and 2,100 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, a mixture solution of 66.4 mL of acetyl chloride and 40.6 mL of propionyl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature and left to stand overnight. 100 mL of methanol and 800 mL of water were added dropwise, followed by introduction of a reaction solution into 10 L of water while vigorously stirring. The white solid was separated by suction filtration, and washed three times with large quantities of water. The white solid was dissolved in methanol, and a white solid obtained by dropping the resulting solution into water was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-9) (acetoxypropylpropionyloxypropylmethylacetylpropionyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (70.1 g).

Synthetic Example 10 Synthesis of acetoxypropylbutyryloxypropylmethylacetylbutyryl Cellulose (C-10)

60 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3) and 2,100 ml of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, a mixture solution of 50.4 mL of acetyl chloride and 73.5 mL of butyryl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature and left to stand overnight. 100 mL of methanol and 800 mL of water were added dropwise, followed by introduction of a reaction solution into 10 L of water while vigorously stirring. The white solid was separated by suction filtration, and washed three times with large quantities of water. The white solid was dissolved in methanol, and a white solid obtained by dropping the resulting solution into water was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-10) (acetoxypropylbutyryloxypropylmethylacetylbutyryl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (74.3 g).

Synthetic Example 11 Synthesis of butyryloxypropylpropionyloxypropylmethylbutyrylpropionyl Cellulose (C-11)

60 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; 14-3) and 2,100 mL of N,N-dimethyl acetamide were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. After it was confirmed that the reaction system became transparent and was completely dissolved, a mixture solution of 60.9 mL of propionyl chloride and 73.5 mL of butyryl chloride was slowly added dropwise, followed by increasing the temperature of the system to 80° C. to 90° C. Stirring was continued for 3 hr, and then the reaction system was cooled to room temperature and left to stand overnight. 100 mL of methanol and 800 mL of water were added dropwise, followed by introduction of a reaction solution into 10 L of water while vigorously stirring. The white solid was separated by suction filtration, and washed three times with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-11) (butyryloxypropylpropionyloxypropylmethylbutyrylpropionyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (69.6 g).

Synthetic Example 12 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-12)

30 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.), 0.74 g of methane sulfonic acid and 57.4 ml of anhydrous acetic acid were measured and put into a 1-liter kneader (a biaxial Werner type kneader equipped with a sigma blade as a stirrer) and stirred at room temperature for 10 min, and then the reaction system was heated to 35° C., and 120 ml of acetic acid was added dropwise over 30 min and maintained for another 2 hr to perform acetylation. 180 ml of water was slowly added dropwise while stirring. This doping solution was introduced into 420 ml of 10% diluted acetic acid while stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-12) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (35.5 g).

Synthetic Example 13 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-13)

30 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.), 0.37 g of sulfuric acid and 57.4 ml of anhydrous acetic acid were measured and put into a 1-liter kneader (a biaxial Werner type kneader equipped with a sigma blade as a stirrer) and stirred at room temperature for 10 min, and then the reaction system was heated to 35° C., and 120 ml of acetic acid was added dropwise over 30 min and maintained for another 2 hr to perform acetylation. 180 ml of water was slowly added dropwise while stirring. This doping solution was introduced into 420 ml of 10% diluted acetic acid while stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-13) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (34.2 g).

Synthetic Example 14 Synthesis of Propionyloxypropylmethylpropionyl Cellulose (C-14)

30 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.), 0.74 g of methane sulfonic acid and 77.2 ml of anhydrous propionic acid were measured and put into a 1-liter kneader (a biaxial Werner type kneader equipped with a sigma blade as a stirrer) and stirred at room temperature for 10 min, and then the reaction system was heated to 35° C., and 120 ml of propionic acid was added dropwise over 30 min and maintained for another 3 hr to perform esterification. 180 ml of water was slowly added dropwise while stirring. This doping solution was introduced into 420 ml of 10% diluted propionic acid while stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-14) (propionyloxypropylmethylpropionyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (34.5 g).

Synthetic Example 15 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-15)

30 g of hydroxypropylmethyl cellulose (trade name: Metolose 90SH-100; manufactured by Shin-Etsu Chemical Co., Ltd.), 0.74 g of methane sulfonic acid and 57.4 ml of anhydrous acetic acid were measured and put into a 1-liter kneader (a biaxial Werner type kneader equipped with a sigma blade as a stirrer) and stirred at room temperature for 10 min, and then the reaction system was heated to 35° C., and 120 ml of acetic acid was added dropwise over 30 min and maintained for another 2 hr to perform acetylation. 180 ml of water was slowly added dropwise while stirring. This doping solution was introduced into 420 ml of 10% diluted acetic acid while stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-15) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are shown in Table 1) as a white powder (33.5 g).

Synthetic Example 16 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-16)

30 g of hydroxypropylmethyl cellulose (trade name: Marpolose 65 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.), 0.74 g of methane sulfonic acid and 57.4 ml of anhydrous acetic acid were measured and put into a 1-liter kneader (a biaxial Werner type kneader equipped with a sigma blade as a stirrer) and stirred at room temperature for 10 min, and then the reaction system was heated to 35° C., and 120 ml of acetic acid was added thereto dropwise over 30 min and maintained for another 2 hr to perform acetylation. 180 ml of water was slowly added dropwise while stirring. This doping solution was introduced into 420 ml of 10% diluted acetic acid while stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-16) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (35.4 g).

Synthetic Example 17 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-17)

30 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.) and 60 ml of acetic acid were commercially obtained, and sufficiently impregnated over 6 hr. The hydroxypropylmethyl cellulose impregnated in the acetic acid was put into a 1-liter kneader (a biaxial Werner type kneader equipped with a sigma blade as a stirrer) while stirring, and the temperature was set at 50° C. 57.4 ml of anhydrous acetic acid was added to the acetification reactor, and then the pressure in the acetification reactor was reduced by a vacuum pump to control the degree of vacuum to 60 Torr. A mixture solution of 0.74 g of methane sulfonic acid and 60 ml of acetic acid was put into the acetification reactor over 30 min to initiate a reaction (the reaction was initiated at a time point when the mixture solution of methane sulfonic acid and acetic acid began to be put). The reaction system was in a boiling state, and the mixed vapor of acetic acid and anhydrous acetic acid was removed. After 60 min of the reaction initiation, the pressure reduction was released. The amount of the solution which had been distilled away until this point was 75 ml. 180 ml of water was slowly added dropwise while stirring. This doping solution was introduced into 420 ml of 10% diluted acetic acid while stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed with large quantities of water. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-17) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (35.8 g).

Synthetic Example 18 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-18)

30 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.), 0.74 g of methane sulfonic acid and 57.4 ml of anhydrous acetic acid were measured and put into a 1-liter kneader (a biaxial Werner type kneader equipped with a sigma blade as a stirrer) and stirred at room temperature for 10 min, and then the reaction system was heated to 35° C., and 120 ml of acetic acid was added dropwise over 30 min and maintained for another 2 hr to perform acetylation. 15 g of 10% calcium acetate was put into the reaction solution to stop the reaction. 180 ml of water was slowly added dropwise while stirring. This doping solution was introduced into 420 ml of 10% diluted acetic acid while stirring, whereupon a white solid was precipitated. The white solid was separated by suction filtration, and washed with large quantities of water, followed by washing with a 0.1% calcium hydroxide aqueous solution. The obtained white solid was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-18) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (36.0 g).

Synthetic Example 19 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-19)

50 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3), 300 ml of ethyl acetate, and 700 ml of acetic acid were measured and put into a 3-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel. The internal temperature was increased to 65° C. while stirring, 161.7 ml of anhydrous acetic acid was added, and 0.49 g of methane sulfonic acid was also added. Stirring was continued for 5 hr, and then the reaction system was cooled to 30° C. 100 ml of water was added to the reaction solution, 150 ml of methanol was subsequently added, and 1.2 L of water was added dropwise, followed by stirring for 10 min. The stirring was stopped and the reaction system was left to stand for 10 min to allow a slurry to settle. 1.5 L of supernatant was taken out, 150 ml of methanol was added thereto while stirring, and 1 L of water was added dropwise, followed by stirring for 30 min. The precipitated white solid was separated by suction filtration, and washed with 1 L of water. The obtained white crystal was dried under vacuum at 100° C. for 6 hr to obtain a desired cellulose derivative (C-19) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (56.2 g).

Synthetic Example 20 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-20)

50 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3), 300 ml of ethyl acetate, and 700 ml of acetic acid were measured and put into a 3-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel. The internal temperature was increased to 65° C. while stirring, 161.7 ml of anhydrous acetic acid was added, and 0.25 g of sulfuric acid was also added. Stirring was continued for 4 hr, and then the reaction system was cooled to 30° C. 100 ml of water was added to the reaction solution, 150 ml of methanol was subsequently added, and 1.2 L of water was added dropwise, followed by stirring for 10 min. The stirring was stopped and the reaction system was left to stand for 10 min to allow a slurry to settle. 1.5 L of supernatant was taken out, 150 ml of methanol was added while stirring, and 1 L of water was added dropwise, followed by stirring for 30 min. The precipitated white solid was separated by suction filtration, and washed with 1 L of water. The obtained white crystal was dried under vacuum at 100 hr for 6 hr to obtain a desired cellulose derivative (C-20) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (55.0 g).

Synthetic Example 21 Synthesis of Propionyloxypropylmethylpropionyl Cellulose (C-21)

50 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3), 300 ml of ethyl acetate, and 700 ml of propionic acid were measured and put into a 3-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel. The internal temperature was increased to 65° C. while stirring, 217 ml of anhydrous propionic acid was added, and 1.23 g of methane sulfonic acid was also added. Stirring was continued for 5 hr, and then the reaction system was cooled to 30° C. 100 ml of water was added to the reaction solution, 150 ml of methanol was subsequently added, and 1.2 L of water was added dropwise, followed by stirring for 10 min. The stirring was stopped and the reaction system was left to stand for 10 min to allow a slurry to settle. 1.5 L of supernatant was taken out, 150 ml of methanol was added thereto while stirring, and 1 L of water was added dropwise, followed by stirring for 30 min. The precipitated white solid was separated by suction filtration, and washed with 1 L of water. The obtained white crystal was dried under vacuum at 100 hr for 6 hr to obtain a desired cellulose derivative (C-21) (propionyloxypropylmethylpropionyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (61.5 g).

Synthetic Example 22 Synthesis of Acetoxypropylmethylacetyl Cellulose (C-22)

50 g of hydroxypropylmethyl cellulose (trade name: Marpolose 90 MP-4000; manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.; H-3), 500 ml of acetonitrile, and 500 ml of acetic acid were measured and put into a 3-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel. The internal temperature was increased to 45° C. while stirring, 161.9 ml of anhydrous acetic acid was added, and 0.37 g of methane sulfonic acid was also added. Stirring was continued for 4 hr, and then the reaction system was cooled to 30° C. 200 ml of methanol was added to the reaction solution, and 1.5 L of water was added dropwise, followed by stirring for 10 min. The stirring was stopped and the reaction system was left to stand for 10 min to allow a slurry to settle. 2.4 L of supernatant was taken out, 500 ml of methanol was added while stirring, and 1 L of water was added dropwise, followed by stirring for 30 min. The precipitated white solid was separated by suction filtration, and washed with 500 mL of water. The obtained white crystal was dried under vacuum at 100 hr for 6 hr to obtain a desired cellulose derivative (C-22) (acetoxypropylmethylacetyl cellulose; the degrees of substitution thereof are described in Table 1) as a white powder (56.2).

Synthetic Example 23 Synthesis of Benzoyloxypropylmethylcellulose Benzoate (C-23)

75 g of hydroxypropylmethyl cellulose (90 MP-4000: manufactured by Matsumoto Yushi-Seiyaku Co., Ltd.), and 2,500 mL of pyridine were measured and put into a 5-liter three-necked flask equipped with a mechanical stirrer, a thermometer, a cooling tube and a dropping funnel, followed by stirring at room temperature. 250 mL of benzoyl chloride was slowly added thereto dropwise under water cooling, followed by stirring at 60° C. for 3 hr. Next, the reaction system was returned to room temperature, and 250 mL of benzoyl chloride was slowly added dropwise, followed by stirring at 60° C. for 3 hr. After the reaction, the reaction system was returned to room temperature, and 1,500 mL of methanol was slowly added dropwise under ice cooling to precipitate a white solid. Supernatant was removed by decantation, 3,000 mL of methanol was added, and the white solid was separated by suction filtration, followed by washing three times with large quantities of the methanol solvent. The obtained white solid was dried under vacuum at 80° C. for 6 hr to obtain benzoyloxypropylmethyl cellulose benzoate (C-23).

Meanwhile, with respect to the compounds obtained in the above, the kinds of functional groups substituted with the hydroxyl groups (R², R³ and R⁶) contained in cellulose, and DSa, MS, and DS_(b)+DS_(C) were observed and determined by ¹H-NMR by using the method as described in Cellulose Communication 6, 73-79 (1999).

<Measurement of Molecular Weights of Cellulose Derivatives>

The number average molecular weight (Mn) and weight average molecular weight (Mw) of the obtained cellulose derivatives were measured. The measurement method thereof will be described below.

[Molecular Weight and Molecular Weight Distribution]

The number average molecular weight (Mn) and the weight average molecular weight (Mw) were determined by using a gel permeation chromatography (GPC). Specifically, N-methylpyrrolidone as a solvent and a polystyrene gel were used, and the molecular weight was obtained by using a reduced molecular weight calibration curve previously obtained from a standard monodispersion polystyrene constitution curve. As the GPC device, HLC-8220 GPC (manufactured by Tosoh Corp.) was used.

The number average molecular weight (Mn), weight average molecular weight (Mw), and degree of substitution were incorporated and shown in Table 1.

TABLE 1 B) Group containing acyl A) group and alkyleneoxy group Hydrocarbon Kind of Kind of C) Acyl Cellulose group acyl alkylene- group DSb + Mn × Mw × Derivative Kind DSa group oxy group MS* Kind DSc 10³ 10³ Synthetic C-1 Methyl 1.95 Acetyl Propyl- 0.29 Acetyl 1.05 62 185 Example group group eneoxy group 1 Synthetic C-2 Methyl 1.84 Acetyl Propyl- 0.22 Acetyl 1.16 135 617 Example group group eneoxy group 2 Synthetic C-3 Methyl 1.47 Acetyl Propyl- 0.24 Acetyl 1.53 114 770 Example group group eneoxy group 3 Synthetic C-4 Methyl 1.45 Acetyl Propyl- 0.25 Acetyl 1.3 120 680 Example group group eneoxy groupl 4 Synthetic C-5 Methyl 1.5 Propionyl Propyl- 0.18 Propionyl 1.5 101 402 Example group group eneoxy Group 5 Synthetic C-6 Methyl 1.43 Acetyl Propyl- 0.19 Acetyl 1.57 67 237 Example group group eneoxy group 6 Synthetic C-7 Methyl 1.45 Butyryl Propyl- 0.25 Butyry 1.29 57 294 Example group group eneoxy group 7 Synthetic C-8 Methyl 1.45 Acetyl Propyl- 0.25 Acetyl 1.55 128 566 Example group group eneoxy group 8 Propionyl Propionyl group group Synthetic C-9 Methyl 1.45 Acetyl Propyl- 0.25 Acetyl 1.55 96 440 Example group group eneoxy group 9 Propionyl Propionyl group group Synthetic C-10 Methyl 1.45 Acetyl Propyl- 0.25 Acetyl 1.47 134 501 Example group group eneoxy group 10 Butyryl Butyryl group group Synthetic C-11 Methyl 1.45 Propionyl Propyl- 0.25 Propionyl 1.18 88 332 Example group group eneoxy group 11 Butyryl Butyryl group group Synthetic C-12 Methyl 1.45 Acetyl Propyl- 0.25 Acetyl 1.53 120 610 Example group group eneoxy group 12 Synthetic C-13 Methyl 1.46 Acetyl Propyl- 0.24 Acetyl 1.5 105 550 Example group group eneoxy group 13 Synthetic C-14 Methyl 1.45 Propionyl Propyl- 0.22 Propionyl 1.45 103 530 Example group group eneoxy group 14 Synthetic C-15 Methyl 1.45 Acetyl Propyl- 0.2 Acetyl 1.56 65 250 Example group group eneoxy group 15 Synthetic C-16 Methyl 1.86 Acetyl Propyl- 0.21 Acetyl 1.04 130 615 Example group group eneoxy group 16 Synthetic C-17 Methyl 1.44 Acetyl Propyl- 0.24 Acetyl 1.54 123 585 Example group group eneoxy group 17 Synthetic C-18 Methyl 1.45 Acetyl Propyl- 0.24 Acetyl 1.55 125 593 Example group group eneoxy group 18 Synthetic C-19 Methyl 1.45 Acetyl Propyl- 0.25 Acetyl 1.45 107 490 Example group group eneoxy group 19 Synthetic C-20 Methyl 1.46 Acetyl Propyl- 0.25 Acetyl 1.46 110 525 Example group group eneoxy group 20 Synthetic C-21 Methyl 1.44 Propionyl Propyl- 0.23 Propionyl 1.58 107 499 Example group group eneoxy group 21 Synthetic C-22 Methyl 1.45 Acetyl Propyl- 0.26 Acetyl 1.53 106 502 Example group group eneoxy group 22 Synthetic C-23 Methyl 1.45 Benzoyl Propyl- 0.25 Benzoyl 1.55 125 751 Example group group eneoxy group 23 *MS represents a molar degree of substitution of alkyleneoxy groups

In Table 1, any one of “B) a group containing an acyl group and an alkyleneoxy group” in the cellulose derivatives C-1 to C-4, C-6, C-12, C-13, C-15 to C-20 and C-22 is a group containing a structure of the following Formula (3-1-1), and any one of “B) a group containing an acyl group and an alkyleneoxy group” in the cellulose derivatives C-5, C-14, and C-21 is a group containing a structure of the following Formula (3-1-2). Further, “B) a group containing an acyl group and an alkyleneoxy group” in the C-7 is a group containing a structure of the following Formula (3-1-3), any one of “B) a group containing an acyl group and an alkyleneoxy group” in the C-8 and C-9 is a group containing a structure of the following formula (3-1-1) and a structure of the following Formula (3-1-2), “B) a group containing an acyl group and an alkyleneoxy group” in the C-10 is a group containing a structure of the following Formula (3-1-1) and a structure of the following Formula (3-1-3), “B) a group containing an acyl group and an alkyleneoxy group” in the C-11 is a group containing a structure of the following Formula (3-1-2) and a structure of the following Formula (3-1-3), and “B) a group containing an acyl group and an alkyleneoxy group” in the C-23 is a group containing a structure of the following Formula (3-1-4).

<Measurement of Melting Initiation Temperature of Cellulose Derivatives>

The melting initiation temperatures of the obtained cellulose derivatives, and Marpolose and Metolose as raw materials were measured. The measurement method thereof will be described below.

[Melting Initiation Temperature (Tm)]

A melting initiation temperature was obtained by measuring the flow initiation temperature of a resin while increasing the temperature at a temperature increasing rate of 5° C./min with a load of 100 kg in a flow tester (manufactured by Shimadzu Corporation). The melting initiation temperature is shown in Table 2.

<Measurement of Thermal Decomposition Initiation Temperature of Cellulose Derivatives>

The thermal decomposition initiation temperatures of the obtained cellulose derivatives, and Marpolose and Metolose as raw materials were measured. The measurement method thereof will be described below.

[Thermal Decomposition Initiation Temperature (Td)]

A thermal decomposition initiation temperature was obtained by measuring a 2% weight reduction temperature of a sample while increasing the temperature at a rate of 10° C./min under nitrogen atmosphere by using a thermogravimetric/differential thermal analysis apparatus (manufactured by Seiko Instruments Inc.). The thermal decomposition initiation temperature is shown in Table 2.

TABLE 2 Cellulose Tm Td Td − Tm derivative [° C.] [° C.] [° C.] Synthetic Example 1 C-1 140 309 169 Synthetic Example 2 C-2 164 331 167 Synthetic Example 3 C-3 175 327 152 Synthetic Example 4 C-4 170 323 153 Synthetic Example 5 C-5 145 318 173 Synthetic Example 6 C-6 164 318 154 Reference Example 1 H-1 215 306 91 Reference Example 2 H-2 240 302 62 Reference Example 3 H-3 240 299 59 Reference Example 4 H-4 258 295 37 Synthetic Example 7 C-7 127 325 198 Synthetic Example 8 C-8 162 324 162 Synthetic Example 9 C-9 163 330 167 Synthetic Example 10 C-10 148 327 179 Synthetic Example 11 C-11 135 325 190 Synthetic Example 12 C-12 170 320 150 Synthetic Example 13 C-13 171 320 149 Synthetic Example 14 C-14 150 320 170 Synthetic Example 15 C-15 170 321 171 Synthetic Example 16 C-16 165 330 165 Synthetic Example 17 C-17 173 320 147 Synthetic Example 18 C-18 175 325 150 Synthetic Example 19 C-19 173 320 147 Synthetic Example 20 C-20 177 325 148 Synthetic Example 21 C-21 152 321 169 Synthetic Example 22 C-22 172 320 148 Synthetic Example 23 C-23 198 333 135

As can be seen from Table 2, it can be seen that the melting initiation temperature of the obtained cellulose derivative has been greatly reduced for Marpolose and Metolose as raw materials. Further, Td-Tm has been greatly increased, which indicates that molding is easily carried out by using the thermoplasticity.

In addition, Td of the hydroxypropylmethyl cellulose phthalate 55 and the hydroxypropylmethyl cellulose phthalate 50 (all manufactured by ACROS Co., Ltd.) having a carboxyl group was measured and all the values were 200° C. or less. From this point, it can be also known that it is preferred that a carboxyl group is not contained.

The solubilities of the obtained cellulose derivative and Marpolose and Metolose as raw materials in water were measured. The measurement method of the solubility will be described below.

[Measurement of Solubility in Water]

Each sample was added to 100 g of water at 25° C. and stirred to confirm whether the sample was dissolved. The results are shown in the following Table 3. Meanwhile, in the following Table 3, an amount of dissolution of 5 g or less is referred to as “insoluble” and an amount of dissolution of more than 5 g is referred to as “soluble”.

TABLE 3 Cellulose derivative Solubility Synthetic Example 1 C-1 insoluble Synthetic Example 2 C-2 insoluble Synthetic Example 3 C-3 insoluble Synthetic Example 4 C-4 insoluble Synthetic Example 5 C-5 insoluble Synthetic Example 6 C-6 insoluble Reference Example 1 H-1 soluble Reference Example 2 H-2 soluble Reference Example 3 H-3 soluble Reference Example 4 H-4 soluble Synthetic Example 7 C-7 insoluble Synthetic Example 8 C-8 insoluble Synthetic Example 9 C-9 insoluble Synthetic Example 10 C-10 insoluble Synthetic Example 11 C-11 insoluble Synthetic Example 12 C-12 insoluble Synthetic Example 13 C-13 insoluble Synthetic Example 14 C-14 insoluble Synthetic Example 15 C-15 insoluble Synthetic Example 16 C-16 insoluble Synthetic Example 17 C-17 insoluble Synthetic Example 18 C-18 insoluble Synthetic Example 19 C-19 insoluble Synthetic Example 20 C-20 insoluble Synthetic Example 21 C-21 insoluble Synthetic Example 22 C-22 insoluble Synthetic Example 23 C-23 insoluble

From Table 3, it can be known that hydroxypropylmethyl cellulose is soluble in water, while the cellulose derivative in the present invention is insoluble in water.

Example 1 Manufacturing of Molded Body Formed of Cellulose Derivative

[Preparation of Test Piece]

The cellulose derivative (C-1) obtained as described above was fed to an injection molding apparatus (manufactured by Imoto machinery Co., Ltd., semi-automatic injection molding apparatus), and molded into a test piece for multipurposes (impact test piece and thermal deformation test piece) having a size of 4×10×80 mm at a cylinder temperature of 200° C., a mold temperature of 30° C. and an injection pressure of 1.5 kgf/cm². The mold temperature was set to 30° C.

Examples 2 to 23 and Comparative Examples 1 to 6

In the same manner as in Example 1, test pieces were prepared by molding the cellulose derivatives (C-2) to (C-23), and the raw materials hydroxypropylmethyl cellulose (H-1) to (H-4) and (H-5) (manufactured by The Dow Chemical Company: ethylcellulose, the degree of ethoxy substitution 2.6), and (H-6) (manufactured by Eastman Chemical Company: celluloseacetatepropionate, the degree of acetyl substitution 0.1 and the degree of propionyl substitution 2.5) as comparative compounds under the molding conditions of Table 4.

<Measurement of Physical Properties of Test Pieces>

With respect to the obtained test pieces, the Charpy impact strength and heat deformation temperature (HDT) were measured by the following method. The results are shown in Table 4.

[Charpy Impact Strength]

In accordance with ISO179, the test pieces molded by injection molding were provided with a notch having the front end of 0.25±0.05 mm and an incident angle of 45±0.5°, and stood still under the conditions of 23° C.±2° C. and 50%±5% RH for 48 hours or more, and then the impact strength was measured by a Charpy impact tester (manufactured by Toyo Seiki Seisaku-Sho, Ltd.) with the edge wise.

[Heat Deformation Temperature (HDT)]

In accordance with ISO75, the temperature was measured when a predetermined bending load (1.8 MPa) was applied to the center of a test piece (in a flatwise direction), the temperature was increased at a constant rate, and thus, a deformation of the center portion reaches 0.34 mm.

TABLE 4 Charpy Cylinder Mold impact Cellulose temperature temperature strength HDT derivative (° C.) (° C.) (kJ/m²) (° C.) Example 1 C-1 200 30 1.9 82 Example 2 C-2 205 30 9.6 96 Example 3 C-3 200 30 15.1 112 Example 4 C-4 200 30 8.1 107 Example 5 C-5 190 30 8.9 75 Example 6 C-6 190 30 8.4 108 Comparative H-1 Not moldable Example 1 Comparative H-2 Not moldable Example 2 Comparative H-3 Not moldable Example 3 Comparative H-4 Not moldable Example 4 Comparative H-5 220 30 13.8 89 Example 5 Comparative H-6 220 30 2.0 80 Example 6 Example 7 C-7 140 30 11.2 65 Example 8 C-8 190 30 10.9 88 Example 9 C-9 190 30 13.4 85 Example 10 C-10 175 30 6.2 91 Example 11 C-11 155 30 10.3 78 Example 12 C-12 200 30 10.5 110 Example 13 C-13 200 30 9.5 112 Example 14 C-14 190 30 9.3 80 Example 15 C-15 200 30 10.9 103 Example 16 C-16 200 30 8.3 108 Example 17 C-17 200 30 8.1 111 Example 18 C-18 200 30 9.2 113 Example 19 C-19 200 30 9.5 114 Example 20 C-20 200 30 10.1 109 Example 21 C-21 190 30 9.2 77 Example 22 C-22 200 30 10 109 Example 23 C-23 210 30 4.2 106

From the results in Table 4, it is understood that hydroxypropylmethyl celluloses (H-1) to (H-4) do not show thermoplasticity, while cellulose derivatives (C-1) to (C-23) in Examples 1 to 23, which are modified with acyl groups in the celluloses, are given an appropriate thermoplasticity and thus, are moldable, as well as exhibit high impact resistance and heat resistance. In addition, although (H-5) and (H-6) in Comparative Examples 5 and 6 were thermo-moldable, it can be understood that cellulose derivatives (C-1) to (C-23) in Examples 1 to 23 are moldable at low temperatures and equivalent or better results are imparted to the cellulose derivatives (C-1) to (C-23) in terms of Charpy impact strength and HDT, when compared to the (H-5) and (H-6).

Industrial Applicability

The cellulose derivative or thermo-molding material of the present invention has excellent thermoplasticity, and thus, may be manufactured into a molded body. Further, a molded body formed by the cellulose derivative or thermo-molding material of the present invention has good impact resistance, heat resistance and the like, and thus, may be used appropriately as component parts such as automobiles, home electric appliances and electric and electronic devices, mechanical parts, materials for housing and construction, and the like. In addition, the cellulose derivative is a plant-derived resin, and a material which may contribute to the prevention of global warming, and thus, the cellulose derivative may replace petroleum-derived resins of the related art. Furthermore, the cellulose derivative and thermo-molding material of the present invention exhibit biodegradability, and thus, are expected to be used as a material with less environmental load.

Although the present invention has been described with reference to detailed and specific embodiments thereof, it is obvious to those skilled in the art that various changes or modifications may be made without departing from the spirit and scope of the present invention.

The present application claims priority from Japanese Patent Application No. 2009-187415 filed on Aug. 12, 2009 and Japanese Patent Application No. 2009-295107 filed on Dec. 25, 2009, the disclosure of which is incorporated herein by reference in its entirety. 

The invention claimed is:
 1. A thermo-molding material comprising a water-insoluble cellulose derivative, wherein the water-insoluble cellulose derivative comprises: A) a hydrocarbon group; B) an alkyleneoxy group containing an acyl group wherein the acyl group has the formula: —CO—Rhd B₁and the alkyleneoxy group has the formula: —R_(B2) —O—wherein R_(B1) represents a hydrocarbon group, and R_(B2) represents an alkylene group having 3 carbon atoms; and C) an acyl group: —CO—R_(c) wherein R_(c) represents a hydrocarbon group, wherein each of A), B) and C) is independently contained in the cellulose derivative and wherein the carboxyl group included in the cellulose derivative is in an amount of 1.0% by mass or less, based on the cellulose derivative, wherein the water-insoluble cellulose derivative has a molecular weight distribution in a range of 1.1 to 10.0 and degrees of substitution of 1.0<DSa<2.5, 0<DSb<1.0 and 0.1<DSc<2.0 wherein DSa is the degree of substitution of the hydrocarbon group A) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a β-glucose ring in a repeating unit, DSb is the degree of substitution of the group containing an acyl group and an alkyleneoxy group B) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a cellulose structure of a β-glucose ring in a repeating unit and DSc is the number of the acyl group C) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a cellulose structure of a β-glucose ring in a repeating unit.
 2. The thermo-molding material of claim 1, wherein A) the hydrocarbon group is an alkyl group having 1 to 4 carbon atoms.
 3. The thermo-molding material of claim 1, wherein A) the hydrocarbon group is a methyl group or an ethyl group.
 4. The thermo-molding material of claim 1, wherein each of R_(B1) and R_(c) independently represents an alkyl group or an aryl group.
 5. The thermo-molding material of claim 1, wherein each of R_(B1) and R_(c)independently represents a methyl group, an ethyl group, or a propyl group.
 6. The thermo-molding material of claim 1, wherein the alkyleneoxy group is a group represented by the following formula (1) or formula (2):


7. The thermo-molding material of claim 1, wherein B) the alkyleneoxy group containing an acyl group is a group containing a structure represented by the following Formula (3):

wherein, R_(B1) represents a hydrocarbon group, and R_(B2) represents an alkylene group having 3 carbon atoms.
 8. The thermo-molding material of claim 1, wherein the carboxyl group included in the cellulose derivative is in an amount of 0.5% by mass or less, based on the cellulose derivative.
 9. A water-insoluble cellulose derivative, comprising a′) an ethyl group; b′) an alkyleneoxy group containing an acyl group wherein the acyl group has the formula: —CO—R_(B1) and the alkyleneoxy group has the formula: —R_(B2)—O—wherein R_(B1) represents a hydrocarbon group, and R_(B2) represents an alkylene group having 3 carbon atoms; and c′) an acyl group: —CO—Rc wherein R_(c) represents a hydrocarbon group, wherein the carboxyl group included in the cellulose derivative is in an amount of 1.0% by mass or less, based on the cellulose derivative, wherein the water-insoluble cellulose derivative has a molecular weight distribution in a range of 1.1 to 10.0 and degrees of substitution of 1.0<DSa<2.5, 0<DSb<1.0 and 0.1<DSc<2.0 wherein DSa is the degree of substitution of the ethyl group a′) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a β-glucose ring in a repeating unit, DSb is the degree of substitution of the alkyleneoxy group containing an acyl group b′) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a cellulose structure of a β-glucose ring in a repeating unit and DSc is the number of the acyl group c′) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a cellulose structure of a β-glucose ring in a repeating unit.
 10. A water-insoluble cellulose derivative, comprising a″) a methyl group; b″) an alkyleneoxy group containing an acyl group wherein the acyl group has the formula: —CO—R_(B1) and the alkyleneoxy group has the formula: —R_(B2)—O—wherein R_(B1) represents a hydrocarbon group, and R_(B2) represents an alkylene group having 3 carbon atoms; and c″) an acyl group: —CO—Rc (Rc represents a hydrocarbon group), wherein the carboxyl group included in the cellulose derivative is in an amount of 1.0% by mass or less, based on the cellulose derivative, and wherein the water-insoluble cellulose derivative has a molecular weight distribution in a range of 1.1 to 10.0 and degrees of substitution of 1.1<DSa<2.5, 0<DSb≦1.5 and 0.1<DSc<2.0 wherein DSa is the degree of substitution of the methyl group a″) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a β-glucose ring in a repeating unit, DSb is the degree of substitution of the alkyleneoxy group containing an acyl group b″) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a cellulose structure of a β-glucose ring in a repeating unit and DSc is the number of the acyl group c″) with respect to the hydroxyl groups at the 2-, 3- and 6-positions of a cellulose structure of a β-glucose ring in a repeating unit.
 11. The cellulose derivative of claim 9, wherein each of Rb1 and Rc independently represents a methyl group, an ethyl group, or a propyl group.
 12. The cellulose derivative according of claim 9, wherein the cellulose derivative has substantially no carboxyl group.
 13. A case for electric and electronic devices, composed of a molding body obtained by molding the thermo-molding material of claim
 1. 14. A method for manufacturing a molded body, comprising: a step of heating and molding the thermo-molding material of claim
 1. 15. The thermo-molding material of claim 1, wherein the molar degree of substitution MS of the alkyleneoxy group of B) is from 0.18 to 0.29.
 16. The thermo-molding material of claim 15, wherein the degree of substitution DSa of A) is from 1.43 to 1.95, the total of the molar degree of substitution MS of the alkyleneoxy group of B) and the degree of substitution DSc of C) is from 1.04 to 1.58.
 17. The cellulose derivative of claim 1, wherein a weight average molecular weight is in a range of 250×10³ to 3,000×10³.
 18. The cellulose derivative of claim 9, wherein a weight average molecular weight is in a range of 250×10³ to 3,000×10³.
 19. The cellulose derivative of claim 10, wherein a weight average molecular weight is in a range of 250×10³ to 3,000×10³. 